Technical
Specification of Nylon-6 Chips
|
1.For Industrial Yarn,Nylon Flim & Engineering plastic use
|
Items
|
Unit
|
Specification
|
|
Relative Viscoslty
|
|
3.45±0.05
|
|
Extractables
|
wt%
|
MAX 0.6
|
|
Moisture Content
|
wt%
|
|
|
Melting Point
|
°
|
215
|
|
Color
|
|
Raw White,Bright
|
|
Size/Shape
|
mm
|
2.0*2.5/cylinder
|
2.For Tire cord yarn use only
|
Items
|
Unit
|
Specification
|
|
Relative Viscoslty
|
|
3.45±0.05
|
|
Extractables
|
wt%
|
MAX 0.6
|
|
Moisture Content
|
wt%
|
|
|
Melting Point
|
°
|
215
|
|
Heat Stabilizer Content
|
PPM
|
850
|
|
Color
|
|
Raw White,Bright
|
|
Size/Shape
|
mm
|
2.0*2.5/cylinder
|
|
Pachage
|
|
Normally 25kg;Supersacks
750kgs
|
Back to Top
1.For Tire cord&Chafer,Industrial fabrics
|
Items
|
Unit
|
930dtex
(840D)
|
1400dtex
(1260D)
|
1870dtex
(1680D)
|
2100dtex
(1890D)
|
|
Breaking Strength
|
N
|
MIN 76
|
MIN 115
|
MIN 150
|
MIN 168
|
|
Elongation at break
|
%
|
MAX 23.5
|
MAX 23.5
|
MAX 23.5
|
MAX 23.5
|
|
Tire deviation
|
dtex
|
±30
|
±30
|
±30
|
±30
|
|
Variation coefficient
of tire
|
%
|
MAX 0.74
|
MAX 0.74
|
MAX 0.74
|
MAX 0.74
|
|
Variation coefficient
of breaking strength
|
%
|
MAX 1.8
|
MAX 1.8
|
MAX 1.8
|
MAX 1.8
|
|
Variation coefficient
of elongation at break
|
%
|
MAX 4.5
|
MAX 4.5
|
MAX 4.5
|
MAX 4.5
|
|
Hot air shrinkage
|
%
|
MAX 7.5
|
MAX 7.5
|
MAX 7.5
|
MAX 7.5
|
|
150° 20Min
|
2.For Marine Rope,webbing Belts,Twine,Cordage,Fishing net
|
Linear Density
|
Tenacity(CN/dtex)
|
Elongation at Break(%)
|
Hot air shrinkage(180°)
|
Color
|
|
930dtex
|
4-8.5
|
19-40
|
17% (U.V.treatment)
|
White
|
|
1400dtex
|
4-8.5
|
19-40
|
17% (U.V.treatment)
|
White
|
|
1870dtex
|
4-8.5
|
19-40
|
17% (U.V.treatment)
|
White
|
|
2100dtex
|
4-8.5
|
19-40
|
17% (U.V.treatment)
|
White
|
Back to Top
|
Nylon 6 Tire Cord Fabric Specification
|
|
Items
|
Unit
|
930dtex/2
(840 D/2)
|
1400dtex/2
(1260 D/2)
|
1400dtex/3
(1260 D/3)
|
1870dtex/2
(1680 D/2)
|
2100dtex/2
(1890 D/2)
|
|
Breaking Strength
|
N
|
MIN 135
|
MIN 208
|
MIN 308
|
MIN 275
|
MIN 310
|
|
Elongation at Load
|
%
|
9.5±0.8
(@4.5KG)
|
9.5±0.8
(@6.8KG)
|
9.5±0.8
(@10.2KG)
|
9.5±0.8
(@9KG)
|
9.5±0.8
(@10.2KG)
|
|
Adhesion(H-Test)
|
N/CM
|
MIN 107.8
|
MIN 137.2
|
MIN 166.6
|
MIN 156.8
|
MIN 166.6
|
|
Unevenness Of Strength
|
%
|
MAX 5.0
|
MAX 5.0
|
MAX 5.0
|
MAX 5.0
|
MAX 5.0
|
|
Unevenness Of Elongation
At Break
|
%
|
MAX 7.5
|
MAX 7.5
|
MAX 7.5
|
MAX 7.5
|
MAX 7.5
|
|
Cord Gauge
|
MM
|
0.55±0.04
|
0.65±0.04
|
0.78±0.04
|
0.75±0.04
|
0.78±0.04
|
|
Twist
|
Z twist
|
T/CM
|
460±15
|
370±15
|
320±15
|
330±15
|
320±15
|
|
S twist
|
460±15
|
370±15
|
320±15
|
330±15
|
320±15
|
|
Dip Pick Up
|
%
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
|
Elongation At Break
|
%
|
22±2
|
23±2
|
23±2
|
23±2
|
23±2
|
|
Moisture Content
|
%
|
MAX 1.0
|
MAX 1.0
|
MAX 1.0
|
MAX 1.0
|
MAX 1.0
|
|
Heat Shrinkage
|
%
|
MAX 8.0
|
MAX 6.5
|
MAX 6.5
|
MAX 6.5
|
MAX 6.5
|
|
Fabric Width
|
CM
|
M±2
|
M±2
|
M±2
|
M±2
|
M±2
|
|
Items
|
Unit
|
930dtex/1
(840 D/1)
|
1400dtex/1
(1260 D/1)
|
1870dtex/1
(1680 D/1)
|
|
Breaking Strength
|
N
|
MIN 67
|
MIN 98
|
MIN 127
|
|
Elongation at Load
|
%
|
7.5±1.0
(@2.3KG)
|
7.0±1.0
(@3.4KG)
|
8.0±1.0
(@4.5KG)
|
|
Adhesion(H-Test)
|
N/CM
|
MIN 49
|
MIN 64
|
MIN 78
|
|
Cord Gauge
|
MM
|
0.32±0.03
|
0.43±0.03
|
0.50±0.03
|
|
Twist
|
T/10CM
|
21±1.5
|
19±1.0
|
16±1.0
|
|
Dip Pick Up
|
%
|
4.2±1.2
|
4.2±1.2
|
4.2±1.2
|
|
Elongation At Break
|
%
|
20±2
|
20±2
|
20±2
|
|
Moisture Content
|
%
|
MAX 0.8
|
MAX 0.8
|
MAX 0.8
|
|
Heat Shrinkage
|
%
|
MAX 4.0
|
MAX 4.0
|
MAX 4.0
|
|
Fabric Width
|
CM
|
M±2
|
M±2
|
M±2
|
|
Items
|
Unit
|
1870dtex/3
(1680 D/3)
|
2100dtex/3
(1890 D/3)
|
|
Breaking Strength
|
N
|
MIN 390
|
MIN 430
|
|
Elongation at Load
|
%
|
10±0.8
(@ 133N)
|
10±0.8
(@ 150N)
|
|
Adhesion(H-Test)
|
N/CM
|
MIN 49
|
MIN 64
|
|
Unevenness Of Strength
|
%
|
MAX 5.0
|
MAX 5.0
|
|
Unevenness Of Elongation
At Break
|
%
|
MAX 7.5
|
MAX 7.5
|
|
Cord Gauge
|
MM
|
0.95±0.04
|
1.05±0.04
|
|
Twist
|
T/M
|
270
|
260
|
|
Dip Pick Up
|
%
|
4.5±1.0
|
4.5±1.0
|
|
Elongation At Break
|
%
|
26.0±2.0
|
26.0±2.0
|
|
Moisture Content
|
%
|
MAX 1.0
|
MAX 1.0
|
Back to Top
|
Nylon
66 Tire Cord Fabric Specification
|
|
Items
|
Unit
|
930dtex/2
(840 D/2)
|
1400dtex/2
(1260 D/2)
|
1400dtex/3
(1260 D/3)
|
1870dtex/2
(1680 D/2)
|
2100dtex/2
(1890 D/2)
|
|
Breaking Strength
|
N
|
MIN 137.2
|
MIN 215.6
|
MIN 313.6
|
MIN 284.2
|
MIN 313.6
|
|
Elongation at Load
|
%
|
8.5±0.6
(@4.5KG)
|
8.5±0.6
(@6.8KG)
|
9.0±0.8
(@10.2KG)
|
8.7±0.6
(@9KG)
|
9.0±0.6
(@10.2KG)
|
|
Adhesion(H-Test)
|
N/CM
|
MIN 107.8
|
MIN 137.2
|
MIN 156.8
|
MIN 156.8
|
MIN 156.8
|
|
CV Of Breaking Strength
|
%
|
MAX 3
|
MAX 3
|
MAX 3
|
MAX 3
|
MAX 3
|
|
CV Of Elongation At
Break
|
%
|
MAX 5
|
MAX 5
|
MAX 5
|
MAX 5
|
MAX 5
|
|
Cord Gauge
|
MM
|
0.53±0.05
|
0.65±0.05
|
0.78±0.05
|
0.74±0.05
|
0.78±0.05
|
|
Twist
|
Z twist
|
T/CM
|
460±15
|
390±15
|
320±20
|
320±15
|
320±20
|
|
S twist
|
460±15
|
370±15
|
320±20
|
330±15
|
320±20
|
|
Dip Pick Up
|
%
|
5.0±0.9
|
5.0±0.9
|
4.5±0.5
|
5.0±0.9
|
4.5±1.0
|
|
Elongation At Break
|
%
|
20.5±2.0
|
21.5±2.0
|
22.0±2.0
|
22.0±2.0
|
22.0±2.0
|
|
Heat Shrinkage
|
%
|
MAX 5.0
|
MAX 5.0
|
MAX 5.5
|
MAX 5.0
|
MAX 5.5
|
Back to Top
|
Items
|
Unit
|
840D/1*840D/1
16EPI*16EPI
|
1260D/1*1260D/1
17EPI*17EPI
|
|
Weft breaking strength
|
kg/19ends
|
110
|
160
|
|
Warp breaking strength
|
kg/15ends
|
90
|
135
|
|
Peel tyre strength
|
kg/inch
|
MIN 18
|
MIN 18
|
|
Dip Pick Up
|
%
|
8±3
|
8±3
|
|
Shrinkage
|
%
|
1.3±0.3
|
1.3±0.3
|
|
Weft elongation at break
|
%
|
12~47
|
20~40
|
|
Warp elongation at break
|
%
|
13~27
|
15~30
|
|
Thickness
|
mm
|
0.57±0.07
|
0.75±0.04
|
|
Weft twsit
|
T/m
|
180±35
|
160±20
|
|
Warp twsit
|
T/m
|
210±55
|
190±40
|
|
Weft heat shrinkage
|
%
|
MAX 3
|
MAX 3
|
|
Warp heat shrinkage
|
%
|
MAX 3
|
MAX 3
|